Material Data Sheet
material no.: | 2.4066 |
UNS no.: | N02200 |
designation: | Alloy 200 |
ASTM B160/564 | DIN 17740 | ||
---|---|---|---|
Ni, min. | 99,0 | Ni + Co, min. 99,2 | |
Cu, max. | 0,25 | 0,25 | |
Fe, max. | 0,40 | 0,4 | |
Mn, max. | 0,35 | 0,3 | |
C, max. | 0,15 | 0,1 | |
Si, max. | 0,35 | 0,2 | |
S, max. | 0,01 | 0,005 | |
Mg, max. | 0,15 | ||
Ti, max. | 0,1 | ||
hot worked | bar | forging ASTM B160 | ASTM B564 |
||
---|---|---|---|
Rm (MPa) | ≥ 415 | ||
Rp 0,2 (MPa) | ≥ 105 | ||
Rp 1,0 (MPa) | |||
A (%) | ≥ 35 | ||
mechanische Eigenschaften | |||
annealed | bar | forging ASTM B160 | ASTM B564 |
bar / forging D ≤ 55 mm DIN 17752 |
|
---|---|---|---|
Rm (MPa) | ≥ 380 | ≥ 370 | |
Rp 0,2 (MPa) | ≥ 105 | ≥ 100 | |
Rp 1,0 (MPa) | ≥ 125 | ||
A (%) | ≥ 40 | ≥ 40 | |
hardness (HBW 2,5/62,5) | max. 130 | ||