Material Data Sheet
material no.: | 2.4360 |
UNS no.: | N04400 |
designation: | Alloy 400 |
ASTM B164/564 | VdTÜV Werkstoffblatt 263 | DIN 17743 | |
---|---|---|---|
Ni, min | 63,0 | 63,00 | Ni + Co, min. 63 |
Cu | 28,0 - 34,0 | 28,0 - 34,0 | 28 - 34 |
Fe | 2,5 max. | 1,00 - 2,50 | 1,0 - 2,5 |
Mn, max. | 2,0 | 2,00 | 2,0 |
C, max. | 0,3 | 0,16 | 0,15 |
Si, max. | 0,5 | 0,50 | 0,5 |
S, max. | 0,024 | 0,020 | 0,02 |
Al, max. | 0,50 | 0,5 | |
Ti, max. | 0,3 | ||
annealed | bar | forging ASTM B164 | ASTM B564 |
bar / forging | bar D ≤ 55 mm DIN 17752 |
---|---|---|---|
Rm (MPa) | ≥ 480 | ≥ 483 | 450 - 600 | ≥ 450 |
Rp 0,2 (MPa) | ≥ 170 | ≥ 172 | ≥ 175 | ≥ 180 |
Rp 1,0 (MPa) | ≥ 210 | ||
A (%) | ≥ 35 | ≥ 30 | ≥ 35 |
hardness (HBW 2,5/62,5) |
max. 150 | ||
thermal expanded | bar cold-drwan D < 12,7 mm ASTM B164 |
bar cold-drawn 12,7 mm ≤ D ≤ 88,9 mm ASTM B164 |
bar / forging VdTÜV Werkstoffblatt 263 |
---|---|---|---|
Rm (MPa) | ≥ 580 | ≥ 600 | 580 - 780 |
Rp 0,2 (MPa) | ≥ 345 | ≥ 415 | ≥ 400 |
Rp 1,0 (MPa) | |||
A (%) | ≥ 10 | ≥ 20 | ≥ 18 |
AV (J) | ≥ 80 | ||